Formation of molybdenum trioxide crystals by electric arc discharge between molybdenum electrodes is considered. Molybdenum oxide crystals were deposited on side surface of anode. Observation of crystals formation zone was used for determination of mainformations stages. Plasma temperature was estimated by optical emission spectroscopy method. The resulting products were studied by X-rays diffraction, time-of-flight laser mass-spectrometry and optical microscopy methods. It was found, that self-organizing vapor-deposition process of MoO3 crystals formation has place. The resulting product is colorless sparkling prisms and platelets, which are mainly consist of orthorhombic a-MoO3 phase. Optical microscopy indicates the formation of closely packed feather-like pin structures by vapor-solid process.
Розглянуто формування кристалів триоксиду молібдену за допомогою електродугового розряду між молібденовими електродами. Кристали формувались на боковій поверхні анода під час горіння вільноіснуючої електричної дуги. Ці кристали являли собою прозорі блискучі призми та пластинки, які складались, головним чином, із орторомбічної фази MoO3. Для визначення основних етапів формування кристалів, їх хімічного складу та структури застосовувались спостереження &зони росту, рентгеноструктурний аналіз, часопролітна лазерна мас-спектрометрія та мікроскопічні дослідження.